磷酸二氢铝

以水和磷酸二氢铝为粘结剂，对氧化硼作为电极防氧化涂层进行了研究。

The antioxidation coating made from boron oxide with water and aluminium dihydrogen phosphate as binders was studied .

研究了水玻璃、磷酸二氢铝、硫酸铝及磷酸二氢铝+硫酸铝复合结合剂对Al2O3-SiO2系浇注料强度和热震稳定性的影响。

Effects of water glass , aluminum dihydrogen phosphate , aluminum sulfate and compound binder containing aluminum sulfate and aluminum dihydrogen phosphate on strength and thermal shock resistance of Al 2O 3-SiO 2 system castables were studied .

利用X射线衍射、红外光谱（IR）等分析手段，对磷酸二氢铝和磷酸二氢铝+硫酸铝复合结合剂的作用机理进行了探讨。

The action mechanisms of aluminum dihydrogen phosphate and the compound binder were approached by XRD and IR analysis .

以高铝矾土、棕刚玉为骨料，矾土粉、SiC粉、石墨为基质料，以磷酸二氢铝和沥青粉为复合结合剂，另加少量αAl2O3微粉，制成了Al2O3-SiC-C捣打料。

Al-2O-3-SiC-C ramming mix was prepared using high alumina bauxite and fused brown corundum as aggregates , bauxite , black SiC and graphite as matrix , aluminum dihydrogen phosphate and pitch as composite binders and adding a small amount of α Al 2 O 3 micropowder .

廉价磷酸二氢铝的制备及在耐火材料中的应用

Preparation of cheap aluminium dihydric phosphate and its application in refractories

三聚磷酸二氢铝Ⅰ型二水物一步合成法及热分解动力学

One-step synthesis and thermal decomposition kinetic of aluminum dihydrogen tripolyphosphate dehydrate I

磷酸二氢铝对高铬耐火泥浆性能的影响

Effect of aluminum dihydrogen phosphate on property of high chromium oxide mortar

制备三聚磷酸二氢铝新工艺研究

New technology for the preparation of aluminium dihydrogen tripolyphosphate

三聚磷酸二氢铝对水中铜离子的吸附动力学

Adsorption Kinetics of Aqueous Copper on Aluminum Dihydrogen Tripolyphosphate

三聚磷酸二氢铝吸附Zn~（2+）的动力学

Adsorption Kinetics of Zn ~ ( 2 + ) on Aluminum Dihydrogen Tripolyphosphate

介绍三聚磷酸二氢铝的性质、合成工艺及应用。

The properties , synthesis process and application of aluminium dihydrogen tripolyphosphate are presented .

提供了廉价磷酸二氢铝的制备方法，介绍了它在耐火材料中的应用。

The Preparation method of cheap aluminium dihydric phosphate and its application in refractories have been intro-duced .

研究主要以磷酸二氢铝无机胶粘剂、陶瓷骨料为原料制备的金属基陶瓷涂层的硬化机理。

The stiffening mechanism of metallic matrix ceramic coating prepared by using acid phosphate binder and ceramic aggregate was studied .

介绍了磷酸二氢铝基料的合成工艺，并讨论了影响该基料组成的因素。

The preparation technology of monobasic aluminum phosphate , an inorganic binder , was described , and factors influencing the composition of inorganic binder were discussed .

研究了以陶瓷颗粒为骨料，磷酸二氢铝为基料，添加多种无机填料的金属用耐磨耐高温涂料。

An abrasion resistant coatings on metal substrates , based on ceramics as aggregate and monobasic aluminum phosphate as binder , mixed with various fillers , has been developed .

故此，研究这些杂质对制备三聚磷酸二氢铝的具体影响具有重要的意义，也是本次毕业论文试验的主要目的。

Therefore , the study of these impurities on the preparation of aluminum dihydrogen tripolyphosphate specific impact is of great significance , is also a test of this thesis the main objective .

试验结果表明：当Al/P的比例为1∶33～14∶3，合成温度为120～140℃时，可获得化学性能优异、产率高的磷酸二氢铝基料。

It has shown that an monobasic aluminum phosphate inorganic binder with excellent chemical property and higher production output can be obtained at a ratio of A1 / P 1 ∶ 3 3 ~ 1 4 ∶ 3 and temperature of 140 ~ 120 ℃ .

用磷酸和氢氧化铝为原料制备三聚磷酸二氢铝二水物。

Aluminum tripolyphosphate hydrate was prepared by phosphoric acid and aluminum hydroxide produced in Guangxi .