流痕

涂复应均匀、牢固、清晰，不应有气泡、流痕、龟裂和剥落等缺陷。

The coating shall be even , fast , clear and free of defects such as air pore , rill mark , chap and spalling .

结合SEM结果，研究了表面缺陷与泡孔形态间的关系；分析了漩涡状流痕和银纹的成因。

It was found that morphology of swirl marks , silver streaks has relation with cell morphology and surface roughness .

产品外观光滑，无粒点，无流痕。

Product appearance of smooth , non-grain points , no flow marks .

硬聚氯乙烯压延片材中气泡与流痕的消除

Eliminator of Bubbles and Flow Marks in Unplasticized Calendered Sheets

铝合金化学抛光流痕的成因及控制

Cause and Control of Striated Effect of Chemical Polishing

每一道光影流痕，都凝固了一个生与死的神话。

Each line of time trace had frozen a myth about living and death .

凹槽流痕在赣北前寒武纪地层中的发现及意义

The discovery of trough marks in the Precambrian strata in northern Jiangxi and their significance

为防止流痕和松垂，建议分三次喷涂。

In order to prevent the flow marking and loosen , suggested to spray three times .

外观表面不可有毛边、刮痕、流痕、亮痕、缩水等不良现象。

No burr , flash , scratch , flow mark , bright speck , shrinkage defects etc on the surface of product .

溶剂型外墙涂料涂层主要是附着性污染，主要表现为雨水流痕。

The stain of the solvent external coating is mainly adhesive stain , the stain of the latex coating is mainly absorbedly one .

在压铸件成型过程中，金属液流动行为复杂，容易产生流痕、气孔、浇不足等缺陷，同时易于造成模具的热疲劳裂纹、冲蚀等，使模具的使用寿命缩短。

During the HPDC process , the filling behavior of liquid metal is very complex , which would cause flow marks , gas porosity , and lack of filling defects . Correspondingly the mold would get thermal fatigue cracks and erosion .

对溢料井的位置和尺寸的设计，以及浇口处流痕、熔料烧焦和气嘴漏气等成型缺陷产生的原因作了分析，并提出了解决措施。

The design of location and size of over flow well , and reasons which resulting in the defects such as flow mark near the gate , melt burned and gas leaking from the gas entrance are analyzed , and the solving measures are put forward .