corrosion product

The higher temperature is , the more the corrosion product is .

随着试验温度升高，断口上的腐蚀产物增多。

Surface of the corrosion product was observed .

观察了腐蚀产物的形貌；

Fe , Si were measured in grain boundary corrosion product .

在晶界的腐蚀产物中含有Fe和Si；

Corrosion product within fatigue crack in salt water and its effect on fatigue crack propagation

盐水中疲劳裂纹内的腐蚀产物及其对疲劳裂纹扩展的影响

The corrosion product on the surface of silver was analyzed by means of XPS .

用X-射线光电子能谱仪（XPS）分析了腐蚀银片表面的腐蚀产物。

Analysis of main constituent of corrosion product on metal surface further proved the previous corrosion mechanism .

通过对金属表面腐蚀产物主要成分的分析，对前述腐蚀机理进行了验证。

Corrosion product of the underground thermal pipeline

埋地高温供水钢管的腐蚀产物分析

The Comparison of Structure and Composition of Corrosion Product for Galvalume in Different Solutions

Galvalume在不同介质中腐蚀产物的形貌和成分分析对比及其对耐蚀性能的影响

The ( accumulation ) of corrosion product results in the cracking of nickel deposit .

腐蚀产物在界面的积累导致镍镀层开裂；

Review of Corrosion Product Films of Cu-Ni Alloys in Seawater

Cu-Ni合金海水蚀产物膜研究进展

Corrosion product film and oil wetting are two great differences in existent rate prediction model in sweet corrosion .

是否考虑原油润湿性和腐蚀产物膜，已成为不同CO2腐蚀预测模型主要的两大差别之一。

Research for Application of the Optimization of Radiation Protection in the Design of a Nuclear Power Plant . - Reduction of Corrosion Product

核电厂实施辐射防护最优化设计中腐蚀产物源项降低的探讨

Analytical results showed that corrosion product contained higher sulphur content and the failure was caused by pitting corrosion .

输送介质-原油是造成管壁腐蚀穿孔，使其失效的主要原因；

In the first stage , anaerobic hydrogen depolarization is predominant and produced iron oxide corrosion product layer ;

初期是厌氧条件下的氢去极化，生成氧化物产物层；

Inhibition Behavior and Synergistic Effect of Inhibitor with Corrosion Product Scale on Low Cr Steel in CO_2-Saturated Solution

低铬钢上缓蚀剂的缓蚀行为及其与腐蚀产物膜的协同作用

The XRD analysis of the corrosion product was made and a hypothesis about corrosion mechanism and some preventive measures were proposed .

根据腐蚀产物的物相分析结果，提出腐蚀机理的假说及防止运行中再次发生腐蚀的办法。

Determination of sulfate radical in molten salt corrosion product of Ni-base superalloy by turbidimetry

硫酸钡比浊法测定镍基高温合金热腐蚀产物中硫酸根

The corrosion product components and corrosion morphology of the Mg-A1-Sn series of magnesium alloys were analysed .

通过扫描电镜和能谱分析了Mg-Al-Sn系列镁合金的腐蚀产物成分及腐蚀形貌。

The corrosion product , the component of the film on the initial copper tube inner surface and the dynamic contrast test are described .

从腐蚀产物的形貌和成分判断该腐蚀属于点蚀，通过备品黄铜管内表面膜成分分析和动态对比试验得出产生腐蚀的主要原因是铜管内存在残碳膜。

Test also discovered that when water temperature in 50 °~ 90 ° C range , CO2 corrosion product has no inhibition action to corrosion .

试验还发现，温度在50～90℃的范围内，CO2腐蚀产物对腐蚀无抑制作用。

XRD analysis revealed that magnesium hydroxide was still the unique corrosion product in the simultaneous presence of dc and ac currents .

XRD分析表明，有交流电干扰时镁阳极腐蚀产物仍然只有Mg（OH）2，这与单纯直流放电时的结果一样。

The corrosion product was exa - mined by means of SEM , EMP and X-ray diffraction .

用SEM，EMP和X射线衍射分析腐蚀产物。

Extracted water , corrosion product and tubing materical were analyzed . The main corrosive factor of oil gathering transportation pipeline was sulfide .

通过对韦2块采出水和腐蚀产物的分析以及对管材的分析，认为集输管线的腐蚀与水中硫化物含量高，以及碳酸氢盐较高，电导率高有关。

The characteristics of corrosion product scale , including thickness , density , content , structure , adhesion , ion selection and stability etc. , can affect corrosion rate ;

腐蚀产物膜的性质，包括厚度、致密度、组成、结构、与基体的粘附力、离子选择性、稳定性等因素都会影响到腐蚀速率；

At70 ℃, an AC impedance spectrum shows that the low frequency can partly reflect the capacitive reactance arc caused by corrosion product film .

70℃时，交流阻抗谱低频部分出现由腐蚀产物膜引起的容抗弧。

The runoff quantity of A3 steel decreases and then increases with pH value of simulated rain increasing , which was explained from change of corrosion product .

A3钢的冲刷量随着模拟雨水pH值的升高表现为先降后升的规律，从腐蚀产物的变化分析了其产生的原因。

The main corrosion product is Fe 2O 3 , showing there are intense aerated water corrosion , oxygen corrosion and electrolytic corrosion in the tube ;

腐蚀产物主要为Fe2O3，表明炉管内存在较为剧烈的汽水腐蚀、氧腐蚀和电解腐蚀；

The inspection after 3 years ' operation has found that the coatings remain intact and there is no accumulation of corrosion product on the floating deck .

运行3年后检查，涂层完好，铝浮盘上无腐蚀产物沉积。

And it was found that the color shown was the effect of light interference of corrosion product film formed on the surface of the electrodeposited zinc steel sheet .

同时发现黑变显示的颜色是由镀锌板表面形成的腐蚀产物膜上产生的光的干涉现象所致。

The medium scale test study of chemical cleaning technique for removing corrosion product ( Fe3O4 ) in secondary side of SG in PWR has been completed .

报道了PWR核电站蒸汽发生器（SG）二次侧腐蚀产物（Fe3O4）化学清洗工艺中型试验研究。